Authors: A. Takahashi, A. Kitamura, R. Seto, Y. Fujita, H. Sakoh, Y. Miyoshi, A. Taniike, Y. Furuyama, T. Murota, T. Tahara
Cu-Ni nano-composite samples showed no excess heat nor meaningfully visible D(H)-loading at room temprature. At elevated temperatures more than 250 deg C, anomalous excess heat lasted for weeks was observed with very large integrated heat as 800 eV per Ni-atom and 600 eV per H-sorption/desorption. Cu0.08Ni0.36/ZrO2 samples gave 10 fold larger excess heat than pure-Ni/ZrO2 samples and 4 fold larger than Cu0.21Ni0.21/ZrO2 samples. Anomalous endothermic effect with abrupt D(H)-desorption was repeatedly observed for pretreatment runs.
Comments: 5 Pages. preprint of submittal to JCMNS for ICCF18 Proceedings
Download: PDF
[v1] 2013-09-10 21:01:13
Unique-IP document downloads: 324 times
Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.
Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.