Authors: Kwangil Kim, Ilman Pak, Kwangmyong Li
ABSTRACT The deposition of MoS2solid lubricant on metal surfaces by non-acid deposition is the most widely used method in aviation and space. The MoS2 film formed by the non-acid deposition is amorphous when the temperature of the matrix is 160 ° or less, and becomes crystalline when the temperature is higher. [2] The amorphous film has a smaller friction coefficient than the crystalline film. [3] In this study, the amorphous film formation conditions of MoS2 were determined theoretically and the friction coefficient was measured in DC cathodic dep
Comments: 4 Pages.
Download: PDF
[v1] 2018-04-27 01:56:03
Unique-IP document downloads: 60 times
Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.
Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.